An Investigation on the Microstructure and Mechanical Properties of Nanocomposites Based on NR/EPDM
- سال انتشار: 1388
- محل انتشار: سومین کنفرانس نانوساختارها
- کد COI اختصاصی: CNS03_051
- زبان مقاله: انگلیسی
- تعداد مشاهده: 4364
نویسندگان
Polymer Engineering Department, Islamic Azad University, South Tehran, Tehran
Department of Rubber, Iran Polymer and Petrochemical Institute, Tehran
Department of Rubber, Iran Polymer and Petrochemical Institute, Tehran
Department of Rubber, Iran Polymer and Petrochemical Institute, Tehran
چکیده
NR/EPDM (75/25) blends containing 1, 3, 5 and 7 phr organo-modified nanoclay (Cloisite15A) were prepared by two-roll mill. The effect of organo-modified layered nanosilicates on microstructure and mechanical properties (tensile strength, abrasion resistance, Fatigue etc.) and also cure characteristics of the nanocomposites were studied. Results suggested the intercalation of polymer chains into the silicate layers which was evidenced by d-spacing results of X-ray diffraction. A further investigation of the nanocomposites microstructure will soon be conducted using TEM. Mechanical properties of the nanocomposites depicted a nearly 40% percents increase respectively in the tensile modulus with 7 wt% nanoclayکلیدواژه ها
Clay; Nanocomposite; Cure time; Scorch time; Mechanical propertiesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.