Dehydration Kinetics and Mechanism of Polyvinyl Alcohol Nanocomposite Hydrogels Containing Hydrophilic Na-Montmorillonite Nanoclay
- سال انتشار: 1388
- محل انتشار: سومین کنفرانس نانوساختارها
- کد COI اختصاصی: CNS03_029
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2479
نویسندگان
Polymer Engineering Group, Faculty of Engineering, Tarbiat Modares University
Polymer Engineering Group, Faculty of Engineering
Immunology Group, Faculty of Medical Science, Tarbiat Modares University
Polymer Engineering Group, Faculty of Engineering, Tarbiat Modares University
چکیده
In this work, polyvinyl alcohol nanocomposite hydrogels containing various loading levels of hydrophilic natural Na-montmorillonite nanoclay, i.e. 0-15 w-t% (based on the dried mass) were prepared via the freezing--thawing cyclic method. The effect of Na-montmorillonite on the gelation process and dehydration kinetic of prepared nanocomposite hydrogels was investigated.The results showed that the gel fraction values of nanocomposite hydrogels were increased by increasing the amount of nanoclay incorporated into them. On the other hand, dehydration results indicated that the dehydration rates of nanocomposite hydrogels had inverse dependency to the nanoclay loading level and direct dependency to the dehydration temperature. Finally, it was concluded that the dehydration mechanism of all prepared hydrogels at 20 C was non Fickian mechanism, while at 37 and 55 C theybehave according the Fickian mechanism.کلیدواژه ها
Nanocomposite hydrogel; dehydration mechanism; Polyvinyl alcohol;Na-Montmorilloniteمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.