Investigation of Nano-SiO2 Effects on High-Volume Fly Ash Concrete
- سال انتشار: 1388
- محل انتشار: دومین کنفرانس بین المللی مقاوم سازی لرزه ای
- کد COI اختصاصی: ICSR02_119
- زبان مقاله: انگلیسی
- تعداد مشاهده: 454
نویسندگان
Graduate M.Sc. Student, University of Sistan Baluchestan
Assistant Professor of Structural Engineering, University of Sistan Baluchestan
Assistant Professor of Structural Engineering, University of Sistan Baluchestan
Graduate B.S. Student, Sharif University of Technology
چکیده
In this paper, laboratory studies have been done on the mechanical properties and microstructure of high-volume fly ash concrete incorporating nano-SiO2. The results were compared with those of ordinary Portland cement (OPC) and of high-volume fly ash concrete (HFC). In this study, in order to determine effects of nano-SiO2 additives on properties of ash mortar, 1%, 2% and 4% of nano-SiO2 was added to the mixes as replacement of cement to investigate their physical properties and micro-structures. In all mixtures, water-binding ratios of 0.5 and 0.6 have been used. Also in all mixtures except OPC samples, constant substitution amount of 40% of ash was proposed. Assessments of these concrete mixes were based on short-term and long-term performance. Compressive strength tests on specimens cured at 3, 7, 28, 56, 90 and 120 days, tensile strength tests on specimens cured at and 28 days and finally SEM test on selected specimens cured at and 120 days were carried out. Results indicated that because of low pozzolanic reaction of fly ash, early strength of HFC decreased considerably. Besides, nano-SiO2 in addition to its effects as ller, because of considerable increase of surface-to-volume, promoted pozzolanic reaction. So, it results in developing the strength of HFC especially in early ages. Also, by increase of curing age of concrete because of activation of fly ash and decrease of Ca(OH)2 due to hydration, strength was developed relative to OPC sample.کلیدواژه ها
compressive strength, fly ash, nano-SiO2, SEMمقالات مرتبط جدید
- بررسی تاثیر استفاده از میراگرها بر پاسخ لرزهای سازه های فولادی با ارتفاع متغیر، تحت اثر زلزله های میدان دور و میداننزدیک
- تاثیر روش الکترواسمزی در تثبیت خاک های نرم اشباع به همراه کربنات کلسیم
- عملکرد سازه های بتنی در زلزله ۲۰۲۰ ازمیر ترکیه
- مطالعه تجربی تعیین مشخصات دینامیکی یک نمونه ساختمان بنایی با استفاده از آزمایش های ارتعاش اجباری و ارتعاش محیطی
- بررسی تاثیر ژیپس و ژئوفوم، بر ویژگیهای خاک رس اشباع
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.