Effect of Mold Material on Cooling Curves of Aluminum during Solidification
عنوان مقاله: Effect of Mold Material on Cooling Curves of Aluminum during Solidification
شناسه ملی مقاله: IMES12_303
منتشر شده در هفتمین کنفرانس بین المللی مهندسی مواد و متالورژی و دوازدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن ریخته گری ایران در سال 1397
شناسه ملی مقاله: IMES12_303
منتشر شده در هفتمین کنفرانس بین المللی مهندسی مواد و متالورژی و دوازدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن ریخته گری ایران در سال 1397
مشخصات نویسندگان مقاله:
Zahra Fallahi - B.Sc. Student- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Hanie Yegane - B.Sc. Student- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Mehdi Malekan - Associate Professor- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Hamed Mirzadeh - Associate Professor- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
خلاصه مقاله:
Zahra Fallahi - B.Sc. Student- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Hanie Yegane - B.Sc. Student- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Mehdi Malekan - Associate Professor- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Hamed Mirzadeh - Associate Professor- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
The effect of cooling rate on the as-cast structure, cooling curve, and solidification time of aluminum was studied. For this purpose, metallic, green sand, and phenolic resin molds were considered. K-type thermocouple was inserted in the middle cross section of each mold and the continuous cooling curves from the pouring temperature were recorded using an accurate data acquisition system. It was revealed that by decreasing the cooling rate, the solidification time increases significantly and the columnar grains become coarser. Subsequently the Chvorinov Rule was used to rationalize the solidification behavior and it was revealed that the mold constant decreases with increasing cooling rate.
کلمات کلیدی: Aluminum; Solidification; continuous cooling curves; Chvorinov Rule