Pitting Corrosion as the Main Cause of Crack Initiation in a Compressor Blade

عنوان مقاله: Pitting Corrosion as the Main Cause of Crack Initiation in a Compressor Blade
شناسه (COI) مقاله: MECHAERO03_145
منتشر شده در سومین کنفرانس بین المللی مهندسی مکانیک و هوافضا در سال 1397
مشخصات نویسندگان مقاله:

Omid Pedram - Department of Mechanical Engineering, University of Zanjan, Zanjan, Iran
Esmaeil Poursaeidi - Department of Mechanical Engineering, University of Zanjan, Zanjan, Iran

خلاصه مقاله:
In this paper, the cause of pitting, its effect on local stress and strain and initiation of the crack which starts from the base of corrosion pit are investigated. The influence of several corrosion pits on the failure of several first - row rotating blades of a few axial-flow compressors which were fractured under fatigue mechanism was studied. The geometry of pits is determined by scanning electron microscopy (SEM) and a finite element model is built to simulate their behaviour. SEM results show that pits forms on the surface of the blade and one of them is the main origin of the crack initiation. Stress and strain distribution around this pit is calculated in order to clarify their effect on crack initiation.

کلمات کلیدی:
pitting corrosion, crack initiation, compressor blade, finite element simulation