Effect of thermal cycles on repairing the edge-cracked aluminum plates by using carbon/epoxy composite patches under tensile load
- سال انتشار: 1395
- محل انتشار: پنجمین کنفرانس بین المللی کامپوزیت
- کد COI اختصاصی: COMPOSIT05_096
- زبان مقاله: انگلیسی
- تعداد مشاهده: 360
نویسندگان
Center of Research in Advanced Materials and Structures,Faculty of Mechanical Engineering, K.N. Toosi University of Technology, Tehran, Iran
Department of Mechanical engineering, Arak Islamic Azad University
چکیده
Performance of the repaired metallic structures during their service life under environmental conditions is a serious concern in using the repair technology. In this study, experimental investigations were done on the repaired edge-cracked aluminum plates using carbon/epoxy composite patches. The repairing processes were conducted to characterize the response of the repaired structures to tensile tests and thermal cycling. Quasi static tensile tests have been conducted to study the first mode of damage of the cracked specimens. Cracks in aluminum specimens with two different lengths are generated. The cracks lengths are 15 mm and 7.5 mm. The plates repaired with 4 layers T300 carbon/epoxy composite patches. The repaired and un-repaired specimens are subjected to 15, 25 and 35 heating cycles with the temperature range between room temperature and 100 oC. The results showed 56% enhancement in the failure load for the repaired specimens in comparison with un-repaired aluminum platesکلیدواژه ها
Composite patch, Thermal cycles, tensile properties, Aluminum plateمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.