A Model to Assess Progressive Fatigue Damage in GFRP Composites with layup systems of [0/±45], [90/±45], and [0/±45/0] over StressCycles
- سال انتشار: 1395
- محل انتشار: پنجمین کنفرانس بین المللی کامپوزیت
- کد COI اختصاصی: COMPOSIT05_083
- زبان مقاله: انگلیسی
- تعداد مشاهده: 364
نویسندگان
Postdoctoral fellow, ۲ Professor, Department of Mechanical Engineering, Ryerson University, ۳۵۰ Victoria Street, Toronto,Ontario M۵B ۲K۳, Canada
Postdoctoral fellow, ۲ Professor, Department of Mechanical Engineering, Ryerson University, ۳۵۰ Victoria Street, Toronto,Ontario M۵B ۲K۳, Canada
چکیده
This study employs an earlier developed stiffness-based model to assess fatigue damage of glass fiber reinforced polymer (GFRP) composites with various layups of [0/±45], [90/±45], and [0/±45/0] under uniaxial stress cycles. The model is constructed based on triphasic damage cracking mechanism in FRP composites and corresponding stiffness reduction of unidirectional plies of 0°, angle-ply laminates of ±45°, and 90° as the number of cycles progresses. The weighting factors η90, η0 and η45 were defined to partition damage of plies in the composite layup systems. Experimental fatigue damage data of [0/±45], [90/±45], and [0/±45/0] composite laminates have fell between the predicted damage curves of 0°, 90° plies and ±45°, 0/±45° laminates over life cycles at various stress levels. Predicted damage results for GFRP laminates showed good agreement with experimental dataکلیدواژه ها
Fatigue damage, Stiffness degradation, GFRP [0/±45] [90/±45] and [0/±45/0] composite layup, Matrix crackingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.