Role of reinforcement content on the fracture behavior of DRA under dynamic loading

  • سال انتشار: 1395
  • محل انتشار: پنجمین کنفرانس بین المللی کامپوزیت
  • کد COI اختصاصی: COMPOSIT05_030
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 395
دانلود فایل این مقاله

نویسندگان

a Hosseini Monazzah

Assistant Professor, Faculty of Mechanical & Energy Engineering, Shahid Beheshti University, A.C.,Tehran, Iran

h Pouraliakbar

MSc, Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran

r Bagheri

Professor, Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran

s.m Seyed Reihani

Professor, Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran

چکیده

Discontinuously reinforced aluminum matrix composites (DRAs) are adequate candidates for substantial class of materials with improved strength, stiffness, fatigue behavior, and wear resistance. Despite these benefits, low impact resistance and damage tolerance restricted the application of DRAs. It is notable that all mechanical properties depend on the shape, size and significantly the volume fraction of second phases which control the fracture behavior of composites. In this research the effect of reinforcement concentration on the impact behavior of hot extruded Al6061-SiC was investigated. Therefore, one monolithic sample beside three types of composite, i.e. Al6061-5 , 10 and 15 vol.% SiC, were fabricated via powder metallurgy route. It was found that an increment on SiC content decreased the impact energy of composite by modifying the fracture surface of samples. Indeed, the enhancement of dislocation density at high strain rate intensified the probability of dislocation locking. By increasing the SiC content, this effect was got highlighted and eventuated in brittle fracture. In this case, the width of shear lips decreased and confirmed the restriction of plastic deformation in metal phase. This limitation in plastic strain was accompanied with modification in fracture surface at high magnification, i.e. an increment in SiCvolume resulted in decrease in voids’ bands, as well as, enhancement in particle cracking within dimples.

کلیدواژه ها

DRA, Composite, Dynamic loading, Fracture, Reinforcement content

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.