Flexural properties of basalt fiber/epoxy composites with nano-ZrO2 enhanced matrix
- سال انتشار: 1395
- محل انتشار: پنجمین کنفرانس بین المللی کامپوزیت
- کد COI اختصاصی: COMPOSIT05_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 354
نویسندگان
MSc Student,Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran
Associate Professor, Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran
PhD Student, Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran
چکیده
In the present research, the effects of adding different percentages of nanozirconia (ZrO2) particles on the flexural properties of epoxy-basalt fiber composites have been investigated. At the first step, the surface of ZrO2 was modified with a silane coupling agent. Fourier transform infrared (FT-IR) data confirmed the bonding between thesilane compound and nanoparticles. Mechanical properties of the composites were investigated under 3-point flexural loading. The flexural strength and flexural mudulus of the nanocomposite specimens containing 1% and 3% nano- ZrO2 have been taken into account at room temperature and the results were compared with the flexural behavior of epoxy-basalt fiber composite. The results revealed that at filler loading of 1 wt.% nano-ZrO2, the flexural strength and flexural modulus of the epoxy-basalt fiber composite enhanced by 16% and 14.2%, respectivelyکلیدواژه ها
Multiscale composite, Basalt fiber, Nano-ZrO2, Flexural strength, Flexural modulusمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.