The Effect of Caspian Sea Water on Corrosion Resistance and Compressive Strength of Reinforced Concrete Containing Different SiO2 Pozzolan
- سال انتشار: 1396
- محل انتشار: ماهنامه بین المللی مهندسی، دوره: 30، شماره: 10
- کد COI اختصاصی: JR_IJE-30-10_006
- زبان مقاله: انگلیسی
- تعداد مشاهده: 390
نویسندگان
Department of Engineering, Damghan Branch, Islamic Azad University, Damghan, Iran
Department of Engineering, Damghan Branch, Islamic Azad University, Damghan, Iran
Civil Engineering Department, School of Engineering, Damghan University, Damghan, Iran
چکیده
Many parameters are influenced by the diffusion of chloride on concrete in marine environments and these can affect concrete quality. In this study, the effect of water to cement ratio of 0.35, 0.40 and 0.45 on corrosion resistance and compressive strength of reinforced concrete was evaluated. Moreover, different percentages of micro silica (SiO2) including 5, 7.5 and 10% were utilized, in order to investigate the effect of pozzolanic materials on the corrosion of steel in concrete. Then cubic samples reinforced with steel bar spacing of 2.5, 5 and 7 cm from the cube surface were made and put in Caspian sea water for 5 months. During this period, corrosion potential of steel was measured by a calomel half cell (SCE). In order to finalize the evaluation of the mechanical strength of the samples, concrete pressure test was conducted and the result showed that after 40, 44 and 59 days for the bars with depth of 2.5, 5 and 7 cm, respectively and the samples prepared with water-cement ratio of 0.35, the corrosion potential was -350V versus SCE, while the compressive strength was approximately 450 kg/cm2. This result showed longer life span of this sample in comparison with other water-cement ratios. By adding micro silica to the samples up to 7.5%, the time for obtaining a corrosion potential of -350V, bars with depth of 2.5, 5 and 7 cm, was 43, 50 and 86 days, respectively, and the compressive strength of this sample was approximately 480 kg/cm2. Consequently, it is arguable that in order to achieve longer life span of corrosion and suitable compressive strength, the optimum ratio of water to cement should be 0.35 and the percentage of pozzolan SiO2 should be 7.5%.کلیدواژه ها
Chloride,Corrosion Potential,Steel Corrosion,Micro silicaمقالات مرتبط جدید
- بررسی به کارگیری سیستم ذخیره سازی انرژی با استفاده از منابع انرژی تجدیدپذیر
- اقدامات لازم برای حفاظت از محیط زیست دریایی
- ارائه طرح مبتنی بر رایانش ابری جهت ارتقاء بهره وری صنایع خودروسازی (مطالعه موردی: مدیران خودرو)
- مروری بر تکنولوژی ماکرویو برای خردایش سنگ های کمیاب
- کاربرد و بکارگیری تکنولوژی های اینترنت اشیا ، یادگیری ماشین و پردازش تصویر در امنیت و کنترل خودرو
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.