Effects of Thermal Procedure on Phase Development in Nano-TiO2 Synthesis Process

  • سال انتشار: 1388
  • محل انتشار: سومین کنگره بین المللی رنگ و پوشش
  • کد COI اختصاصی: ICCC03_071
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 2662
دانلود فایل این مقاله

نویسندگان

K Badii

Department of Environmental Researches, Institute for Color Science and Technology.

B Mazinani

School of Metallurgy and Material Engineering, Iran University of Science and Technology.

S Shaker

Department of Chemistry, Science Faculty, Shahid Rajaiee University

چکیده

Nano-TiO2 has many applications in science and technology, especially as a photocatalyst.In this research, nano-TiO2 synthesized by sol-gel method and applied for environmental proposes to degrade organic colorants and mineralize colored wastewater. TiO2 has two main phases, anatase and routile. The routile phase is normally used as inorganic pigment to produce paints and ceramics, but its anatase form is able to oxidize organic compound in a photo-catalytical process. The synthesis process is very sensitive to thermal procedure and any change would cause different final product structure. The experiments have shown that a fast increasing to temperature range of 450 to 550 °C and continued to calcinate in this range of temperature is the best procedure to product anatase nano-TiO2 for catalytical proposes.

کلیدواژه ها

Nano-TiO2, Nano-photo-catalyst, Waste water treatment, anatase structure, Degradation, Organic colorants

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.