Chemical Synthesis of Nano-Crystalline Nickel-Zinc Ferrite as a Magnetic Pigment

  • سال انتشار: 1388
  • محل انتشار: سومین کنگره بین المللی رنگ و پوشش
  • کد COI اختصاصی: ICCC03_069
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 2191
دانلود فایل این مقاله

نویسندگان

Sh Jebeli Moeen

Advanced Material Research Center, Material and Energy Research Center, Karaj, Iran Department of Inorganic Pigments and Glazes, Institute for Color Science and Technology (ICST), Tehran, Iran

M.R Vaezi

Advanced Material Research Center, Material and Energy Research Center, Karaj, Iran

A.A Yousefi

Department of Inorganic Pigments and Glazes, Institute for Color Science and Technology (ICST), Tehran, Iran

چکیده

The nickel-zinc ferrite nano-crystalline were prepared by chemical synthesis. Zinc nitrate, nickel nitrate, iron nitrate hydrate, citric acid and ethylene glycol were used as precursor materials. Crystallization behavior of the precursor was studied by Xray diffraction (XRD). Nanoparticle phases can change amorphous to spinel ferrite depending on the calcination temperature. Morphological and structural properties were investigated by scanning electron microscopy (SEM). The FTIR spectra show that the main broad metal–oxygen band in 1000–100cm-1 range assigned to the spinel phases. The powder density was measured using a helium pycnometer is about 5.73 g/cm3. Magnetization measurements were carried out on an alternative gradient magnetometer (AGM), which revealed saturation magnetization of the samples were strongly dependent on the calcination temperature and particle size of the sample. Therefore, with increasing particle size, saturation magnetization increases. Other results indicated a correlation between pigment color and calcinations temperature. The color of the pigment changes from reddish- brown to drak- brown depending on the calcination temperature.

کلیدواژه ها

Chemical synthesis, Nano-crystalline, Magnetization

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.