Effect of Nano Powder Fe2O3 on UV-Vis Spectroscopy of Sodium Silicate Glasses

سال انتشار: 1388
محل انتشار: سومین کنگره بین المللی رنگ و پوشش
کد COI اختصاصی: ICCC03_018
زبان مقاله: انگلیسی
تعداد مشاهده: 3127

دانلود فایل این مقاله

نویسندگان

B MirhadI

Department of Material Engineering, Imam Khomeini International University, Qazvin, Iran

B Mehdikhan

Department of Material Engineering, Imam Khomeini International University, Qazvin, Iran

M Markaz

Department of Inorganic Pigments and Glazes, Institute for Color Science and Technology

چکیده

In this study, the effect of various oxidation states of iron on optical spectroscopy of sodium silicate glasses has been investigated. So as, different amount of iron oxide were added as xFe2O3.Na2O.2SiO2 compound to sodium disilicate glasses and were melted in different temperatures Iron commonly exists as an equilibrium mixture of ferrous ions, 2+ Fe , and ferric ions, 3+ Fe , in glass. 3+ Fe ions shows strong absorption in UV light and yellow color is appeared, while 2+ Fe has an absorption band in NIR, consequently has blue color. With increasing ferric iron, amount of 3+ Fe ions will increase and yellow color develops. With increasing melting temperature of glass, amount of 2+ Fe ions will increase and bluish-green color develops. As a result, some variation has been observed in optical spectroscopy UVVis of produced glasses.

کلیدواژه ها

Nano powder Fe2O3 , Spectroscopy UV-Vis, Sodium silicate glass

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.