Silicon Nanoparticle Fabricated via High Energy Ball Milling as a High Capacity Anode for Lithium-ion Batteries
- سال انتشار: 1396
- محل انتشار: کنفرانس و کارگاه بین المللی نانوفناوری و نانو پزشکی NTNM 2017
- کد COI اختصاصی: NTNM01_034
- زبان مقاله: انگلیسی
- تعداد مشاهده: 574
نویسندگان
Department of Semiconductor, Materials and Energy Research Center (MERC), Karaj, P.O. Box: ۳۱۷۸۷-۳۱۶, Iran
Department of Semiconductor, Materials and Energy Research Center (MERC), Karaj, P.O. Box: ۳۱۷۸۷-۳۱۶, Iran
Department of Semiconductor, Materials and Energy Research Center (MERC), Karaj, P.O. Box: ۳۱۷۸۷-۳۱۶, Iran
Department of Semiconductor, Materials and Energy Research Center (MERC), Karaj, P.O. Box: ۳۱۷۸۷-۳۱۶, Iran
Materials and Energy Research Center (MERC), Karaj, P.O. Box: ۳۱۷۸۷-۳۱۶, Iran
چکیده
Silicon nanostructure is potentially studied as a negative electrode in lithium ion batteries. In this study, micro-grain silicon was mechanically activated during 6 hours using the planetary ball mill and was prepared the silicon nanoparticle with the average particle size of 230 nm. Morphological and chemical identification of silicon nanoparticles were confirmed using the FE-SEM and XRD analyses. In order to investigation of the electrochemical performance of the silicon anode, Galvanostatic charge state was applied, achieving the specific charge capacity of 0.4 mAh/cm2 at 0.2 mA/cm2 current density. Moreover, the CV curves showed that the rate of electron transfer is so fast the traced back to the rate of mass transfer.کلیدواژه ها
silicon; ball mill; anode; lithium-ion batteryاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.