The Effect of Heat Treatment on Weld Strength of Al- Steel Joints with Different Thicknesses
- سال انتشار: 1396
- محل انتشار: ششمین کنفرانس بین المللی مهندسی مواد و متالورژی و یازدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن علمی ریخته گری
- کد COI اختصاصی: IMES11_101
- زبان مقاله: انگلیسی
- تعداد مشاهده: 542
نویسندگان
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak
Department of Electrical Engineering, Faculty of Engineering, Arak University, Arak, Iran.
چکیده
In the present study the effect of heat treatment on bond strength and intermetallic formation in dissimilar Aluminum-steel joints was investigated. Whereas the softer metal (Aluminum) was thinner, all samples were fractured from weld zone. Therefore, it was possible to evaluate the bond strength of the welds even when the bond strength of the weld exceeded the base material. It was observed that as welded sheets have the bond strength equivalent to the base material and the toughness were so low. After heat treatment for 1 hour, the bond strength and elongation increased considerably but thereafter increased time of heat treatment led to degradation of weld strength and elongation.کلیدواژه ها
friction stir welding, heat treatment, intermetallic, bond strengthمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.