Effects of Zr element and Solidification Parameters on the microstructure and tensile properties of Al-7%Si-0.5%Mg Alloy
- سال انتشار: 1395
- محل انتشار: چهارمین کنفرانس بین المللی آلومینیوم ایران IIAC۲۰۱۶
- کد COI اختصاصی: IIAC04_063
- زبان مقاله: انگلیسی
- تعداد مشاهده: 632
نویسندگان
M.sc.student, department of Metallurgy and Materials south Tehran branch, Islamic Azad University, Tehran, Iran
Professor,School of Metallurgy and Materials, College of Engineering, University of Tehran, Tehran, Iran
M.sc.student ,School of Metallurgy and Materials, College of Engineering, University of Tehran, Tehran, Iran
چکیده
In this investigation, experiments were carried out to study the relationship of master alloy Al–5Zr and solidification parameters in Al-7wt%Si-0.5wt%Mg casting with various thicknesses under the same solidification condition. The optimum level of Zr as Al–5Zr grain refiner was found to be ( 0.03 wt.%), respectively. It was found that 0.03 wt% Zr addition could refine the microstructure significantly and modify the eutectic Si from plate-like morphology to fiber converted. The results show that the Increasing cooling rate through reduced sections, decreases grain size and dendrite arm spacing ,but Zr-refined specimens showed lowest sensitivity to cooling rate. The relationships between the microstructre and cooling rate have investigated. The microstructural characterization was carried out by optical microscopy and image analysis. meachanical properties also have investigated at various thicknesses.کلیدواژه ها
Aluminium alloys; Casting; grain refinerمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.