Daynamic nature of diffuson during solidification

  • سال انتشار: 1395
  • محل انتشار: چهارمین کنفرانس بین المللی آلومینیوم ایران IIAC۲۰۱۶
  • کد COI اختصاصی: IIAC04_009
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 511
دانلود فایل این مقاله

نویسندگان

M.H Avazkonandeh-Gharavol

Department of Materials and Polymer Engineering, Faculty of engineering, Hakim Sabzevari University, Sabzevar, P.O. Box ۳۹۷, Iran.

M Haddad-Sabzevar

Department of Metallurgy and Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Azadi Square, P.O. Box ۹۱۷۷۵-۱۱۱۱, Mashhad, Iran

H Fredriksson

Department of Materials Science and Engineering, Royal Institute of Technology, Brinellvägen ۲۳, ۱۰۰۴۴, Stockholm, Sweden

چکیده

Some of the mechanisms which determine the extent of microsegregation during solidification of metallic alloys are based on the diffusion in the solid, so deep knowledge about diffusion is essential for studying the microsegregation. The aim of this research is therefore to elucidate the nature of diffusion during the solidification. For this purpose, Al-4.8 wt% Cu alloy was selected as model alloy. Solidification tests were carried out using a differential thermal analysis (DTA) furnace capable of quenching samples during solidification. Cooling rate was selected as 5 K/min and samples were quenched from predetermined temperatures during the solidification. Copper concentration profiles in the primary phase were measured by scanning electron microscope (SEM) equipped with an energy dispersive spectroscopy (EDS) detector. The concentration profiles were also calculated by numerical modeling and compared to the experimental profiles. According to the results it concluded that the diffusion coefficient has higher values than the tabulated ones at the begging of solidification. The results were discussed according the current theory of solidification.

کلیدواژه ها

Solidification; Microsegregation; Phase Diagram; Diffusion Coefficient; Vacancy

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.