Study of milling effect on particle size and mechanical properties ofWC-Co composite
- سال انتشار: 1395
- محل انتشار: کنفرانس ملی نانو ساختارها،علوم و مهندسی نانو
- کد COI اختصاصی: NCNNN01_142
- زبان مقاله: انگلیسی
- تعداد مشاهده: 517
نویسندگان
MSc, Materials and Energy Research Center, Karaj, Iran
Assistant Professor, Materials and Energy Research Center, Karaj, Iran
چکیده
The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratio by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350 ̊C at a rate of temperature rise 50 ̊C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly full dense was obtained for sample. The calculated mechanical properties revealed optimum amounts of 14.25 GPa hardness, 772 MPa bending strength and 13.86 Pa.m1/2 fracture toughness. The XRD analysis indicated the dominant indentified phases was WC. The FESEM observation showed presence of Co between ceramic particles as binder.کلیدواژه ها
Tungsten carbide, Cobalt, SPS, Mechanical propertiesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.