Thin palladium composite membrane with high reversibility of CO2 poisoning
- سال انتشار: 1396
- محل انتشار: چهارمین کنفرانس هیدروژن و پیل سوختی
- کد COI اختصاصی: H2FC04_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 630
نویسندگان
Chemical Engineering Faculty, Sahand University of Technology, Tabriz, Iran
Chemical Engineering Faculty, Sahand University of Technology, Tabriz, Iran
Chemical Engineering Faculty, Islamic Azad University, Tabriz Branch, Iran
چکیده
A palladium membrane using the electroless plating technique (ELP) was prepared for the isolation and purification of hydrogen from gas mixture. The membrane performance in the presence of CO2 was investigated. Depending on operating conditions, hydrogen flux from the membrane was in the range of 0.012-0.023 mol.m-2.s-1. The results of the GC analysis showed that at a feed concentration of 10% CO2 and a difference pressure of 1-2 bar, no traces of CO2 in the permeate side was observed.However, due to the occupation of the catalytic active sites by carbon dioxide, hydrogen permeation through the membrane decreased. At the concentration of 20% CO2 and a difference pressure of 1-2bar, the peak of methane in the permeate side was detected by the GC analysis, which is related to the diffusion of carbon from the feed side to the permeation side. In order to recovery the poisoned membrane, it was exposed to hydrogen in 500 °C for an hour. The obtained results show that hydrogen permeation of the membrane was returned to the state before poisoning, confirming the successful recovery of membrane.کلیدواژه ها
Palladium membrane, Electroless plating technique, Poisoning, Membrane recoveryمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.