Mechanical behavior of Clay-Calcium carbonates/epoxynanocomposites

  • سال انتشار: 1390
  • محل انتشار: سومین کنفرانس بین المللی مواد فوق ریزدانه و نانوساختار
  • کد COI اختصاصی: UFGNSM03_270
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 372
دانلود فایل این مقاله

نویسندگان

MAYSAM NAZERI

Department of Chemical Engineering, Faculty of Engineering, Tehran University, P.O. Box ۱۱۳۶۵/۴۵۶۳, Tehran, Iran

SEYEDJAVAD AHMADI

Nuclear Science and Technology Research Institute, End of North Karegar Ave., P.O. Box ۱۴۳۹۹۵۱۱۱۳, Tehran, Iran

SEYED MOHAMMAD ALI MOOSAVIYAN

Department of Chemical Engineering, Faculty of Engineering, Tehran University, P.O. Box ۱ ۱۳۶۵/۴۵۶۳, Tehran, Iran

MAHDI KHAKSARI

Department of Chemical Engineering, Faculty of Engineering, Tehran University, P.O. Box ۱۱۳۶۵/۴۵۶۳, Tehran, Iran

چکیده

In this study, Clay-Calcium carbonate sepoxy nanocomposites with content of 1, 3, 5 wt.% Nano-Clay/NanoCalcium carbonate particles were prepared by shear mixing followed by ultrasonicto improvement of nanoparticles dispersion in the epoxy matrix. The microstructures of the nanocomposites were characterized by means of scanning electron microscopy (SEM). It was found the uniform dispersion of Nano-Calcium Carbonate and exfoliation of Nano-Clay in resulting nanocomposites. The mechanical behavior of nanocomposites was investigated with tensile test. It could be concluded which nanocomposites exhibit the best tensile strength.

کلیدواژه ها

:Nano-clayS; nanocomposites; epoxy, Nano-calcium carbonate; Mechanical properties

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.