EFFECT OF NANO STRUCTURE WC POWDERADDITION ON THE WEAR RESISTANCE OF70CR STEEL
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 348
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_054
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
In this research, Fe-WC composite was successfully synthesized by injecting WC-Nano structure powders in to the molten 70Cr, Steel. Microtungsten carbides was ball milled with 300rpm speed and 10:1 ball to powder weight ratio under argon atmosphere for 50 hours to produce WC-Nano structure powder. The main grain size of 25nm was obtained for milled WC on the basis of XRD profile analysis. Steel sample with 0 and 2.5 weight percentage of nano structure WC were prepared via centrifugal molding. Microstructure was studied by scanning electron microscope. EDX indicated WC dispersion in steel matrix. Wear resistance test clearly showed that in the sample which include tungsten carbide, Wear resistance was improved.
کلیدواژه ها:
نویسندگان
ARYA PARWANEH
Nano and advanced materials department, Material and Energy research Center, Meshkindasht, Karaj, lran
MOHAMMAD REZA RAHMPOUR
Ceramic department, Material and Energy research Center, Meshkindasht, Karaj, lran
MOHAMMAD ZAKER
Ceramic department, Material and Energy research Center, Meshkindasht, Karaj, lran