SYNTHESIS OF AL2Oa-ZRBa NANOCOMPOSITE POWDERBY MECHANICAL ALLOYING
- سال انتشار: 1390
- محل انتشار: سومین کنفرانس بین المللی مواد فوق ریزدانه و نانوساختار
- کد COI اختصاصی: UFGNSM03_034
- زبان مقاله: انگلیسی
- تعداد مشاهده: 420
نویسندگان
Ceramic Department, Materials and Energy Research Center, P.O. Box. ۳۱۷۸۷/۳۱۶, Karaj, Iran
Ceramic Department, Materials and Energy Research Center, P.O. Box. ۳۱۷۸۷/۳۱۶, Karaj, Iran
SEYED) ALI TAYEBIFARD)Semiconductor
Department, Materials and Energy Research Center, P.O. Box: ۳۱۷۸۷/۳۱۶, Karaj, Iran
چکیده
In this research Al2O3-ZrB, nanocomposite powder was successfully synthesized by high energy ball milling of ZrO2, B2O3 and Al powders at nominal room temperature. Effect of milling time was investigated. XRD, TEM and SEM analysis were performed for monitoring of the composite formation, microstructure and morphology of the milled powders. Results showed that this composite was formed between 20-25 h of milling time. High energy milling led to the smaller grain size and larger lattice strain. The mean grain size and microstrain of 11.7 nm and 0.2% were obtained for 30 h milled sample on the basis of Reitveld refinement method that is in consistent with TEM observations. SEM images showed that very fine particles with the spherical morphology were procured after 15 h of milling. Further milling up to 30 hled to agglomeration of primary particlesکلیدواژه ها
Zirconium diboride, Alumina, Mechanical Alloying, Nanocompositeمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.