Influence of annealing on anisotropic crystallinestructure of HDPE cast flms

  • سال انتشار: 1395
  • محل انتشار: فصلنامه پلی اولفین ها، دوره: 3، شماره: 1
  • کد COI اختصاصی: JR_POJ-3-1_005
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 615
دانلود فایل این مقاله

نویسندگان

Ali Yadegari

Faculty of Processing, Iran Polymer and Petrochemical Institute, P.O. Box ۱۴۹۷۵/۱۱۲, Tehran, Iran Leibniz-Institut für Polymerforschung Dresden e. V., Hohe Str. ۶, D-۰۱۰۶۹ Dresden, Germany

Jalil Morshedian

Faculty of Processing, Iran Polymer and Petrochemical Institute, P.O. Box ۱۴۹۷۵/۱۱۲, Tehran, Iran

Hossein-Ali Khonakdar

Faculty of Processing, Iran Polymer and Petrochemical Institute, P.O. Box ۱۴۹۷۵/۱۱۲, Tehran, Iran Leibniz-Institut für Polymerforschung Dresden e. V., Hohe Str. ۶, D-۰۱۰۶۹ Dresden, Germany

Udo Wagenknecht

Leibniz-Institut für Polymerforschung Dresden e. V., Hohe Str. ۶, D-۰۱۰۶۹ Dresden, Germany

چکیده

High density polyethylene (HDPE) flms were produced using cast flm extrusion process with different draw ratios, ranging from 16.9 to 148.8. Morphology, crystallinty and orientation state of crystalline andamorphous phases of the cast flms were investigated using scanning electron microscopy (SEM), differentialscanning calorimetry (DSC) and polarized Fourier transform infrared spectroscopy (FTIR) analyses, respectively.The anisotropic crystalline structures of row-nucleated lamellar morphology were observed for the flms producedwith high draw ratios. The crystalline phase axes orientation functions were found to be signifcantly dependent onthe applied draw ratios. As expected, annealing increased the crystallinity and melting point temperature (Tm) of thecast flms and on the other hand, it also enhanced the crystalline phase orientation. However, the results revealedthat annealing also promoted non-twisted lamellar structures, since it increased the fc values (c-axis orientationfunction) and decreased the fa values (a-axis orientation function) simultaneously. Additionally, it was found thatthe annealing induced enhancement in c-axis orientation function was more signifcant for the cast flms with lowerdraw ratios, therefore, it was dependent on the draw ratio. Polyolefns J 3:1-9

کلیدواژه ها

HDPE; cast flm extrusion; crystal orientation; annealing; crystallinity

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.