An Investigation on the Bond Strength of Aluminum Strips in the Presence of Brass Mesh after Cold Roll Bonding

  • سال انتشار: 1395
  • محل انتشار: مجله شکل دهی مواد، دوره: 3، شماره: 2
  • کد COI اختصاصی: JR_IJMF-3-2_005
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 481
دانلود فایل این مقاله

نویسندگان

E. Tolouei

Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran

M. R. Toroghinejad

Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran

F. Ashrafizadeh

Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran

چکیده

In this study, the presence of brass mesh on the bond strength of aluminum (AA1050) strips in the cold roll bonding (CRB) process was investigated. The influence of various process parameters including reduction in thickness, pre-rolling annealing, initial thickness of the strips, and post-rolling annealing was also considered. After CRB process, peeling test was carried out and peeled surfaces were examined by optical and scanning electron microscopes (SEM). Energy dispersive spectroscopy (EDS) analysis also, revealed that there was neither diffusion zone, nor formation of intermetallic at the interface of aluminum and brass wires after annealing at 643 K. It was found out that, by increasing the amount of reduction and initial thickness, the bond strength of the layers was increased. Furthermore, pre-rolling and post-rolling annealing treatments at 643 K increased the bond strength.

کلیدواژه ها

Bond strength, Cold roll bonding, Peeling test, Composite

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.