Polyurethane/Graphene Nano-Composites with Gas Barrier Properties

  • سال انتشار: 1391
  • محل انتشار: دهمین سمینار بین المللی علوم و تکنولوژی پلیمر
  • کد COI اختصاصی: ISPST10_763
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 333
دانلود فایل این مقاله

نویسندگان

Poria Kaveh

Polymer Engineering Center, Islamic Azad University, South Tehran Branch, Tehran, Iran.

Mehrzad Mortezaei

Polymer Engineering Center, Islamic Azad University, South Tehran Branch, Tehran, Iran.

Mehdi Barikani

Department of Polyurethane, Faculty of Polymer Science, Iran Polymer and Petrochemical Institute, Tehran, Iran.

Atefeh Kaveh

Islamic Azad University, Shiraz Branch, Shiraz, Iran.

چکیده

Polymeric materials have long been utilized for packaging applications. However, overwhelming demands in the marketplace have put significant pressure for materialdevelopers to pursue novel routes to manufacture low cost packaging films with greatly improved barrier properties [1].The emergence of polymer nano-composites introduces a newopportunity to improve barrier properties of polymers. When the nano-platelets are well exfoliated, in addition to theimproved barrier property, polymer nano-composites usually exhibit enhanced mechanical properties and better thermalstability [1, 2]. Graphene has a high basal plane elastic modulus, E ≈ 1 TPa; ultimate strength, σ ∼ 130 GPa; and room temperature chargecarriermobility, μ ≈ 10 000 cm2/V s. Adding highly exfoliated carbon layers can significantly alter mechanical and electrical properties of polymers at extremely small loading [3]. Unlikecarbon nanotubes that can provide similar mechanical and electrical benefits, these impermeable two-dimensional sheetscan reduce gas permeability of host membranes [4]. In the present study, the effect of graphene on gas barrier performance of thermoplastic polyurethane (TPU)/graphene nano-composites was investigated. For this propose, TPU was reinforced with various contents of graphene (0-2 wt.%)through solvent blending procedure. The physical and mechanical properties of the prepared nano-composites wereinvestigated through transmission electron microscopy (TEM), wide angle X-ray reflectance diffraction (WAXD), dynamic mechanical analysis (DMA) and differential scanning colorimetery (DSC), as well as, tensile strength and gas permeability measurements.

کلیدواژه ها

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.