Cure behavior of polysulfide-based sealants filled with carbon black at different levels as recognized from rheological studies
- سال انتشار: 1395
- محل انتشار: دوازدهمین سمینار بین المللی علوم و تکنولوژی پلیمر
- کد COI اختصاصی: ISPST12_564
- زبان مقاله: انگلیسی
- تعداد مشاهده: 570
نویسندگان
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, Isfahan, Iran
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, Isfahan, Iran
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, Isfahan, Iran
Department of Resin and Additives, Institute for Color Science and Technology, Teheran, Iran
چکیده
Polysulfide sealants with different content of carbon black as filler (15, 20 and 25 phr) were prepared and their rheological properties were investigated. Viscoelastic properties of samples were evaluated by rheometric mechanical spectrometer (RMS). Gel point for samples with different filler content under temperature- and time-sweep mode was assessed. The results show that sealant with 20 phr carbon black has minimum gel point temperature and the gel time at 90 C for this sample was less than a few minutesکلیدواژه ها
Polysulfide Sealant-Carbon Black-Gel Point -Viscoelastic Propertiesاطلاعات بیشتر در مورد COI