Effect of Silica Antiblock on Thermo-oxidative Degradation of Polyethylene Film Grades: Rheological Investigation
- سال انتشار: 1395
- محل انتشار: دوازدهمین سمینار بین المللی علوم و تکنولوژی پلیمر
- کد COI اختصاصی: ISPST12_013
- زبان مقاله: انگلیسی
- تعداد مشاهده: 339
نویسندگان
Department of Research and Development, Jam Petrochemical Company, Asaluyeh, Iran
Department of Research and Development, Jam Petrochemical Company, Asaluyeh, Iran
Department of Research and Development, Jam Petrochemical Company, Asaluyeh, Iran
چکیده
Silica is added to polyethylene film grades to roughen their surface and thereby to prevent layers of the film from sticking. Silica usually has impurities like iron oxide facilitating degradation of the polyethylene resin.Rheological investigation of thermo-oxidative degradation of polyethylene resin was carried out using a Rheometric Mechanical Spectrometer. Obviously, observed increases in dynamic modulus and viscosity are attributed to formation of long chain branching (crosslinking). Our results indicated that the presence of silica increase the rate of degradation of polyethylene, remarkablyکلیدواژه ها
Polyethylene, silica, degradation, crosslinking, rheological parametersاطلاعات بیشتر در مورد COI