STRUCTURE AND OPTICAL STUDY OF VANADIUM TELLURITE GLASSES CONTAINING POTASSIUM OXIDE
- سال انتشار: 1395
- محل انتشار: مجله تحقیقات کاربردی، دوره: 2، شماره: 2
- کد COI اختصاصی: JR_ARJ-2-2_002
- زبان مقاله: انگلیسی
- تعداد مشاهده: 500
نویسندگان
Department of Physics, Parand Branch, Islamic Azad University, Parand, Iran
چکیده
Vanadium Tellurite Glasses samples were successfully fabricated by TeO2,V2O5 and K2CO3 precursor. TeO2-V2O5 glasses were melted at 750 oC todetermine the optical and structural study. The optical absorption spectra ofglassy have been recorded in the wavelength range 300-900 nm by UVVisiblespectrophotometer. In addition the temperature glass transition (Tg,)of glasses has been determined by Differential Scanning Calorimetry(DSC), confirming the amorphous nature of samples. The amorphous phasewas characterized by X-ray diffraction analysis. The SEM results showedthat the particle size of the samples was decreased with increasing annealingtemperature from 3.4 μm to 117 nm. The optical absorption spectra showedthat there is not sharply defined in the glass samples, in accord with theiramorphous nature. DSC data showed that Tg shifts to higher temperatureswith increasing heating rate.کلیدواژه ها
Vanadium Tellurite, Glasses, amorphous, morphological studyاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.