Synthesis methods of ZrC nano particles

سال انتشار: 1395
محل انتشار: اولین سمپوزیوم بین المللی نانو تکنولوژی
کد COI اختصاصی: ISON01_052
زبان مقاله: انگلیسی
تعداد مشاهده: 746

دانلود فایل این مقاله

نویسندگان

Mina Saeedi Heyd

Faculty of Materials & Manufacturing Processes, Malek Ashtar University of Technology, Tehran, Iran

Jalaleddin Ghezavati

Young Researchers and Elite club, Bonab Branch, Islamic Azad University, Bonab, Iran

Mahdi Abbasgholipour

Assistant Professor, Department of Mechanical Engineering, Bonab Branch, Islamic Azad University, Bonab, Iran

Behzad Mohammadi Alasti

Assistant Professor, Department of Mechanical Engineering, Bonab Branch, Islamic Azad University, Bonab, Iran

چکیده

Zirconium carbide (ZrC) is one of the ceramic materials that has the melting point above 3400 °C, high hardness and good thermo-mechanical properties and is considered as one of the best known candidates for high temperature applications. Many methods have been reported for the synthesis of ZrC powder that can be noted to carbothermal reduction of ZrO2 at high temperature, sol-gel, low temperature synthesis by the reaction of magnesium in ZrO2-Mg-CH4, mechanical alloying and high temperature combustion synthesis. In this article tried to investigate about all methods that have been used for the synthesis of this material.

کلیدواژه ها

Zirconium carbide (ZrC), Powder synthesis, High temperature application

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.