Effect of SiC nanofibers on the oxidation resistance of graphite
- سال انتشار: 1395
- محل انتشار: اولین سمپوزیوم بین المللی نانو تکنولوژی
- کد COI اختصاصی: ISON01_005
- زبان مقاله: انگلیسی
- تعداد مشاهده: 714
نویسندگان
Faculty of Materials and Manufacturing Technology, Malek-Ashtar University of Technology, Tehran, Iran
Faculty of Materials and Manufacturing Technology, Malek-Ashtar University of Technology, Tehran, Iran
Faculty of Materials and Manufacturing Technology, Malek-Ashtar University of Technology, Tehran, Iran
چکیده
In an attempt to improve the oxidation resistance of graphite, a coating containing SiC nanofibers was developed on a graphite substrate using the pack cementation and slurry painting techniques at 1600 °C temperature. The microstructure of the coating was characterized by X-ray diffraction and scanning electron microscopy. The thermal shock tests of the coated samples were accomplished at 1500 °C. Results show that a gradient C–SiC transition layer with about 500 μm in thickness was formed at the graphite-coating interface. SiC nanofibers with the diameter in the range of 30-70 nm were detected on the coating whose growth was attributed to the gas phase reaction of SiO with CO. The oxidation test results discovered that the SiC nanofibers serve an important role in the oxidation resistance so that the mass loss of the secondary coating with SiC nanofibers was 17% compared to 72% for the initial coating without SiC nanofibers.کلیدواژه ها
SiC, Nanofibers, Graphite oxidation resistance, Polycarbosilaneمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.