Experimental study on sandwich panels with Edge Insert under Pull out load

سال انتشار: 1394
محل انتشار: کنفرانس دو سالانه بین المللی مکانیک جامدات تجربی
کد COI اختصاصی: WMECH03_033
زبان مقاله: انگلیسی
تعداد مشاهده: 693

نویسندگان

Professor, Center of Excellence for Research in Advanced Materials and Structures, Faculty of Mechanical Engineering, K.N. Toosi University of Technology, Tehran, IRAN

H Fatehi

Department of Mechanical Engineering, South Tehran Branch, Islamic Azad University, Tehran, Iran

چکیده

The purpose of this study is to evaluate the failure load of edge inserts in sandwich structures under pull out conditions. Specimens were constructed from PVC foam and glass-epoxy laminates. The insert that used in this investigation is a special types of insert that upper composite skin of sandwich panel are stayed on the upper flange of the insert. This action reinforces the junction between the insert and the sandwich panel. To study the mechanical behavior of the specimens under Pull out load, two types of joints these joints with and without potting material are examined. The experiments showed that the failure modes of the sandwich panels with insert are a combination of different modes, such as debonding of the insert from the laminates and the core, cracks in the core, composite laminates failure and when the insert debonded from the bottom skin, the junction is failed and the load at this point named as the failure load of at the junction. Comparison of the failure loads in the reinforced and non-reinforced specimens are showed that the potting material leads to 74.5% increase in the failure load.

کلیدواژه ها

Sandwich panel, Edge Insert, Pull out, potting material, Reinforce

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.