Effect of cold working amount and annealing temperature on softening kinetics of commercial purity aluminum

  • سال انتشار: 1393
  • محل انتشار: سومین کنفرانس بین‌المللی آلومینیوم ایران IIAC2014
  • کد COI اختصاصی: IIAC03_082
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 817
دانلود فایل این مقاله

نویسندگان

m Piriaee

Department of Mechanical Eng, Khaje Nasir Toossi University of Technology, Tehran, Iran

m Pazhuhandeh

Department of Mining and Metallurgical Eng, Amirkabir University of Technology, Tehran, Iran

a Farzadi

Department of Mining and Metallurgical Eng, Amirkabir University of Technology, Tehran, Iran

چکیده

In the present research, the effect of cold working amount and annealing temperature on the microstructure and softening kinetics of commercially pure aluminium strips have been studied. Kinetics of softening is evaluated by Avrami-Johnson equation. In this equation, k and n refer to constant and exponent of Avrami equation, respectively. Reduction of area in cold – rolled commercially pure aluminium strips were 20% and 40% to investigate the degree of cold rolling on kinetics of softening. Also, to evaluate the effect of annealing temperature, the aluminium strips were annealed in 320 oC, 360 oC and 400 oC. The results indicate that by increasing the annealing temperature the values of k and n increase. The values of n and k increase when the degree of cold working increases.

کلیدواژه ها

cold–working; annealing treatment; recrystallization; Avrami equation; kinetics of recrystallization

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.