Effects of Zr addition on corrosion resistance of CrN films prepared in a magnetron sputtering system
- سال انتشار: 1394
- محل انتشار: ششمین کنگره بین المللی رنگ و پوشش
- کد COI اختصاصی: ICCC06_015
- زبان مقاله: انگلیسی
- تعداد مشاهده: 700
نویسندگان
Nanomaterials and Nanocoatings Department, Institute for Color Science and Technology, Tehran, Iran
Surface Coating and Corrosion Department, Institute for Color Science and Technology, Tehran, Iran
چکیده
CrN and CrZrN films were produced by a planar type reactive sputtering system. The potentiodynamic polarization measurements in 0.5 M NaCl solution indicated that CrZrN films show better corrosion resistance than CrN film. Corrosion cu rrent density of CrZrN films was lower than CrN which means better corrosion resistance of CrZrN films. Moreover, co rrosion speed of CrZrN coated steel was lower that uncoated sample which means that Zr has positive effects on corrosion resistance of CrN films.کلیدواژه ها
Magnetron sputtering- CrN- CrZrN- Physical vapor deposition- Corrosion resistanceمقالات مرتبط جدید
- سنتز نانو ماده اکسیدگرافن و بررسی تاثیر آن بر روی مقاومت شیمیایی رنگ آلکیدی
- پیش بینی نرخ های تولید چندفازی (نفت، گاز و آب) با استفاده از روش های یادگیری ماشین: مرور بر روش ها و کاربردها
- روشهای کنترل داده محور در مهندسی شیمی
- بررسی جداسازی گاز پروپیلن از پروپان در غشای ۶FDA-durene با استفاده از روش شبیه سازی مولکولی
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.