Structural and Magnetic Properties of Nickel Ferrite Nanoparticles: Effect of Annealing

سال انتشار: 1393
محل انتشار: پنجمین کنگره بین المللی نانو و فناوری نانو (ICNN2014)
کد COI اختصاصی: ICNN05_654
زبان مقاله: انگلیسی
تعداد مشاهده: 454

نویسندگان

Department of physics , University of guilan, Rasht, Iran

چکیده

Nickel ferrite nanoparticles were prepared by co-precipitation method. The prepared powder was annealed at 500°C,700°C, 900°C and 1100°C. The powders were characterized by the X-ray diffraction technique (XRD), FourierTransform Infrared (FTIR), and the magnetic behavior studied by Vibrating Sample Magnetometer (VSM). XRDanalysis showed that nickel ferrite has a spinel structure. Crystallite size calculatedfrom XRD peak broadening resultedin the largest crystallite size of 24 nm. The FT-IR spectra of NiFe2O4showed strong absorption peaks around 600 and400 cm-1 which are typical for the cubic spinel crystal structure. Magnetic measurements showed that magnetizationand coercivity increases when annealing temperature is increased.

کلیدواژه ها

Nickel ferrite; co-precipitation; spinel structure

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.