Effects of calcination temperature on characterization of barium ferrite nanopowder produced via wet chemical route
- سال انتشار: 1393
- محل انتشار: پنجمین کنگره بین المللی نانو و فناوری نانو (ICNN2014)
- کد COI اختصاصی: ICNN05_644
- زبان مقاله: انگلیسی
- تعداد مشاهده: 401
نویسندگان
School of Metallurgy and Materials Engineering, University of Tehran , Tehran, Iran
School of Metallurgy and Materials Engineering, University of Tehran , Tehran, Iran
School of Metallurgy and Materials Engineering, University of Tehran , Tehran, Iran
چکیده
This investigation dealt with the synthesis of nanocrystalline barium ferrite (BaFe12O19) powders through coprecipitationroute. The effects of calcination temperature on the phase composition and morphology of the sampleswere studied. X-ray diffraction results revealed that barium ferrite phase starts to form at calcination temperature of800˚C and fully formed when the temperature increased to 1000˚C. Field emission scanning electron microscopeanalysis showed that the prepared sample annealed at 900˚C contains barium ferrite plate-like particles with an averageparticle size of 60 nm. It was also observed that barium ferrite crystallites stack in side of each other due to theirmagnetic attraction.کلیدواژه ها
Calcination; Co-precipitation; Nanopowder; Barium ferriteاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.