Effect of milling time and microwave sintering on the microstructure and micro-hardness of nano-structured Cordierite

سال انتشار: 1393
محل انتشار: پنجمین کنگره بین المللی نانو و فناوری نانو (ICNN2014)
کد COI اختصاصی: ICNN05_611
زبان مقاله: انگلیسی
تعداد مشاهده: 487

نویسندگان

Materials & energy Research Centre, Alborz, Iran

چکیده

The purpose of this research is to investigate the sintering of cordierite (34.86 wt% Al2O3, 51.36 wt% SiO2and 13.78 wt% MgO) nano-grains synthesized by mechanical activation route. Samples were prepared by the high-energyball milling of the starting powders followed by conventional and microwave sintering at 1390°C. SEM observationsillustrated the equiaxed nano-grains of cordierite with an average grain size of 30 nm for samples sintered in microwave.With the increase of milling time, samples sintered at 1390°C in microwave furnace obtained lower porosity, higherdensity and microhardness than those sintered at the same temperature in conventional furnace. Sample milled for 30 hand sintered in microwave furnace at 1390°C obtained the maximum microhardness of 1089±5 kg/mm2.

کلیدواژه ها

Microwave; Milling; Micro-hardness; Microstructure; Nano Cordierite

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.