The Effect of Al2O3 Nanoparticle Addition on the Coating Behavior of Al-based Suspensions in Producing Nanocomposite Hollow Spheres

سال انتشار: 1393
محل انتشار: پنجمین کنگره بین المللی نانو و فناوری نانو (ICNN2014)
کد COI اختصاصی: ICNN05_436
زبان مقاله: انگلیسی
تعداد مشاهده: 394

نویسندگان

Faculty of Materials Science and Engineering, K.N.Toosi University of Technology

چکیده

The present study carried out fluidized bed coating of Al‐based powder‐binder suspension onto a polymersubstrate. The effect of the nanoparticle additive and process time was investigated for coating process efficiency andcoating characteristics. It was found that efficiency decreased as the processing time increased, but the coatingthickness increased as the processing time and amount of binder increased. For a sample with 1.5 wt. % of binder, asthe nanoparticle content changes from 2.5 to 7.5 wt.%, the coating thickness decreases from 351 to 310 μm. This issueabout efficiency is 61.11% (for 2.5 wt. %) and 52.78% (for 7.5 wt. %).

کلیدواژه ها

Fluidizied bed coating; Al nanocomposite; Efficiency; Nanoparticle; Hollow Sphere; Binder

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.