Synthesis of latex Nano particles and polymer /clay Nano-composite particles andinvestigation of their effect on water absorption and the flexural strength of cement
- سال انتشار: 1393
- محل انتشار: پنجمین کنگره بین المللی نانو و فناوری نانو (ICNN2014)
- کد COI اختصاصی: ICNN05_160
- زبان مقاله: انگلیسی
- تعداد مشاهده: 443
نویسندگان
Department of chemical engineering , Iran university of science and technology, Tehran, Iran
Department of chemical engineering , Iran university of science and technology, Tehran, Iran
Department of chemical engineering , Iran university of science and technology, Tehran, Iran
چکیده
two type of acrylic polymer latex and their polymer/clay composite were synthesized by emulsionpolymerization. The effects of adding latexes and concentration of clay in the Nano-composite latexes on the waterabsorption and the flexural strength of cement were analyzed. The maximum flexural strength was achieved forsamples that modified with composite, containing 3% of Nano clay/polymer ratio. The amount of water absorbed bythe polymer modified samples decreased more than 65 percent. The suitable distribution of clay particles in thepolymer was shown by TEM micrographکلیدواژه ها
Nano clay, Nano composite, latex, permeability, flexural strengthاطلاعات بیشتر در مورد COI