PTES MODIFIED SILICA FILMS; SYNTHESIS AND CHARACTERIZATION

سال انتشار: 1394
محل انتشار: دومین همایش ملی تکنولوژی های نوین در شیمی و پتروشیمی
کد COI اختصاصی: TCPCO02_043
زبان مقاله: انگلیسی
تعداد مشاهده: 723

دانلود فایل این مقاله

نویسندگان

m ramezani

Division of Nanotechnology and Advanced Materials,

m.r vaezi

Division of Semiconductors, Materials and Energy Research Center, Karaj, Iran

a Kazemzadeh

Division of Semiconductors, Materials and Energy Research Center, Karaj, Iran

چکیده

The present paper describes dip coated water repellent silica coatings on the glass substrates using phenyltriethoxysilane (PTES) as a co-precursor, tetraethoxysilane (TEOS) as a precursor, ethanol (EtOH) as a solvent and ammonium hydroxide (NH4OH) as a catalyst via sol-gel method. In order to study the influence of the modifying agent on the hydrophobic properties of the silica films, the molar ratio of PTES/TEOS (H) was varied between 0.05 and 1.2. The static water contact angle values of the silica coatings increased up to 133º with an increase in the H value from 0 to 0.05. However, with further increase in H value, the water contact angle and surface modification decreased whereas the size of nanoparticles increased from 36 to 45 nm. The hydrophobic silica films were characterized by atomic force microscopy (AFM), fourier transform infrared spectroscopy (FTIR),contact angle measurement (CA), and field emission scanning electron microscopy (FE-SEM) images.

کلیدواژه ها

Silica film, PTES, Sol-gel method, Wettability

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.