Tribological And Corrosion Behavior Of(Ti,Al)CN/DLC Coating
- سال انتشار: 1393
- محل انتشار: چهارمین کنفرانس بین المللی کامپوزیت
- کد COI اختصاصی: COMPOSIT04_096
- زبان مقاله: انگلیسی
- تعداد مشاهده: 730
نویسندگان
MSc .student, Department Of Materials Eng., Faculty Of Eng., Shahrekord Uni., Shahrekord, Iran
Assistant professor, Department Of Materials Eng., Faculty Of Eng., Shahrekord Uni., Shahrekord, Iran
Assistant professor, Naghsh-E- Jahan University, Baharestan, Isfahan, Iran
MSc Engineering Materials, Marine Industry-Department Of Subsurface Vessels, Shahin Shahr, Isfahan,Iran
چکیده
Composite (Ti, Al)CN/DLC coatings were prepared on substrate of 316 stainless steel by cathodic arc method using two TiAl bars as targets and C2H2 and N2 mixing gas. structure of the coatings were evaluated using XRD andRaman spectroscopy methods. The XRD results revealed presence of TiC, Ti3AlN and Ti2N crystalline phases in the coats. Besides friction coefficient and wear rate of the coatings were investigated using pin-on-disc test method. Frictionand wear studies showed that friction cofficient and wear rate of coating was 0/2 and 9×10-8 mm3/N.m Respectively. Surface wear of samples after wear test is observed by SEM. Corrosion behaviour of the coated samples is tested bypotentio-dynamic method. Surface morphology of the samples before and after corrosion tests is observed using by SEM and AFM micrograph.کلیدواژه ها
DLC, Tribological Behavior , Corrosion propertiesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.