Structural and characteraization of WO3 thin films prepared by sol-gel method
- سال انتشار: 1394
- محل انتشار: دومین کنفرانس ملی توسعه علوم مهندسی
- کد COI اختصاصی: AIHE09_034
- زبان مقاله: انگلیسی
- تعداد مشاهده: 691
نویسندگان
Department of Engeneering Islamic Azad University, nour branch Nour, Iran
چکیده
in this study WO3 thin films prepared by sol gel method at 250 and 450°C. these films were characterized by XRD, SEM and spectrophotometry analysis. The film were annealed at 250°C was amorphous and high temperature annealing crystallizes them. According to the scanning electron microscopy (SEM) image, the films annealed at 250˚C were dense. Moreover, the particles were uniformly distributed on them. The samples annealed at 250˚C represent the maximum transmission at a wavelength of 400 nm, having a good blue color. The samples' transmittances decreased as the annealing temperature increased.کلیدواژه ها
Electrochrimic, sol gel, WO3 , thin filmمقالات مرتبط جدید
- بررسی به کارگیری سیستم ذخیره سازی انرژی با استفاده از منابع انرژی تجدیدپذیر
- اقدامات لازم برای حفاظت از محیط زیست دریایی
- ارائه طرح مبتنی بر رایانش ابری جهت ارتقاء بهره وری صنایع خودروسازی (مطالعه موردی: مدیران خودرو)
- مروری بر تکنولوژی ماکرویو برای خردایش سنگ های کمیاب
- کاربرد و بکارگیری تکنولوژی های اینترنت اشیا ، یادگیری ماشین و پردازش تصویر در امنیت و کنترل خودرو
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.