Polymorphism Studies in PVDF/PEG Membranes

سال انتشار: 1393
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 700

فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

ICHEC15_622

تاریخ نمایه سازی: 19 تیر 1394

چکیده مقاله:

Poly (vinylidene fluoride) (PVDF) membranes were prepared by the phase inversion method using N,N-dimethylacetamide (DMAc) as polymer solvent and water as non-solvent. Different crystal form of Poly (vinylidene fluoride) (PVDF) were studied after PVDF membranes preparation as function of coagulation bath temperature and PEG inclusion in polymer dope solution. The low temperature coagulation bath (25 ˚C) mainly resulted to β phase formation, whereas higher temperature coagulation bath (60 ˚C) resulted to formation of more structures of α phase. Besides, the β phase content in PVDF decreased via 5 wt% PEG inclusion into PVDF.

نویسندگان

Amir Fadaei

Faculty of science, Iran Polymer and Petrochemical Institute (IPPI),۱۴۹۶۵/۱۱۵ Tehran, Iran

Ali Salimi

Faculty of science, Iran Polymer and Petrochemical Institute (IPPI),۱۴۹۶۵/۱۱۵ Tehran, Iran

Mojgan Mirzataheri

Faculty of science, Iran Polymer and Petrochemical Institute (IPPI),۱۴۹۶۵/۱۱۵ Tehran, Iran

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Abbrent S., Plestil J., Hlavata D., Lindgren J., Tegenfeldt J., ...
  • Zheng J., He A., Li J., Han C. _ "Polymorphism ...
  • Salimi A., Yousefi A. A., _ Confo rmational Changes and ...
  • نمایش کامل مراجع