As water shut off treatments with polymer gel applied in oil reservoirs, degelling motivation within a reservoir might be desired. In this work, a hydrogel was prepared by crosslinking of aqueous solutions of a sulfonated polyacrylamide and chromium (III) acetate. In order to investigate the effective factors (gel age, degelling agent/crosslinker concentration ratio, degelling agent/gel weight ratio and crosslinker concentration) and their interactions central compositedesign, as a most popular form of response surface methodology was used. Among the investigated factors, crosslinker concentration, degelling agent/crosslinker concentration ratio and degelling agent/gel weight ratio were identified as main effects, respectively. The results impliedthat increase of crosslinker concentration and degelling agent/gel weight ratio caused an increase of degelation time where increase of degelling agent/crosslinker concentration ratio caused a decrease of degelation time. Moreover, degelling agent/gel weight ratio and crosslinker concentration showed strong interactions.

polymer gel, degelation time, degelling agent, central composite design