Synthesis and characterization of perovskite membrane for hydrogen separation at high temperature
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 764
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_148
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
Asymmetrical thin membrane of (BCYb) was synthesized by liquid-citrate method and the membrane was prepared by pressing followed by sintering. The phase structure of powder was characterized by X-ray diffraction and thermogravimetry (TG). Scanning electron microscopy (SEM) was used to investigate the microstructure of sintered membrane. Hydrogen permeation fluxes (JH2) were measured as a function of temperature and hydrogenpartial pressure (PH2) gradient. The high hydrogen permeation flux of the 1.63 mm BCYb membrane at 900 °C for mixture of 60% H2/He was 0.043 ml/cm2.s.
کلیدواژه ها:
نویسندگان
Marzieh Heidari
Chemical engineering department, Sharif University of technology, Tehran, Iran
Akbar Zamaniyan
Gas department, Research Institute of Petroleum Industry, Tehran, Iran
Aliakbar Safe kordi
Chemical engineering department, Sharif University of technology, Tehran, Iran
Ensieh Ganji Babakhani
Gas department, Research Institute of Petroleum Industry, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :