Mechanical Properties of Acrylic solvent-based traffic paints

سال انتشار: 1393
محل انتشار: چهارمین کنگره بین المللی پوشش های حمل و نقل
کد COI اختصاصی: ICAPC04_008
زبان مقاله: انگلیسی
تعداد مشاهده: 1276

نویسندگان

Iran Polymer and Petrochemical Institute (IPPI)

چکیده

Stress-strain analysis (SSA) and abrasion resistance of solvent based traffic paints as a common category in road marking materials are important issues for evaluation of a road marking durability in its service life. In this study, various solvent based acrylic paints were formulated in such a way that the general paint properties e.g. no pick-up time, viscosity, reflectance 45̊/0˚ and hiding power were optimized. Three paint formulations contain different amounts of resin (20, 30 and 40 wt %) and silica in particle size of 400 nm. In optimum amount of the resin (i.e. 30 wt %) two other paints, one without silica (S-18-WS) and the other with fine silica in 40 nm (S-18-fine) were prepared. SSA on free film and abrasion resistance on intact films of the paints onto a substrate were evaluated using tensile and Taber abrasion tests respectively.The analysis results showed that the highest work of rupture (area under stress-strain curve) corresponds to lowest weight loss in Taber abrasion test. In other words SSA results can be used to interpret the abrasion resistance of solvent based traffic paints.

کلیدواژه ها

Road marking, Traffic paint, Taber abrasion resistance, SSA, Mechanical properties

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.