The effects of post curing process on the physical properties of Glass fiber /phenol –formaldehyde molded composites

  • سال انتشار: 1392
  • محل انتشار: همایش ملی پژوهش های کاربردی در علوم و مهندسی
  • کد COI اختصاصی: TIAU01_761
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 694
دانلود فایل این مقاله

نویسندگان

r.m rudd

Department of chemical engineering, Takestan Branch , Islamic Azad University, Takestan, Iran

s.r ghafarian

Faculty of Polymer engineering, Amir Kabir University of Technology, Tehran, Iran

a taherkhani

Department of physics, Takestan Branch , Islamic Azad University, Takestan, Iran

چکیده

The effect of post curing on two important physical properties of a Glass/Phenol- Formaldehyde (Novolac) composite is investigated. Samples are molded and postcured in different procedures. The Their Tg are measured using DMA test. The weight loss of sampled during post curing are determined as well. Result suggestthat the Post curing has a significant effect on TG of thermoset resin and increases it considerably. This ,in turn, will raise thermal resistance and dimensional stability of the composite

کلیدواژه ها

Post Curing, Glass / phenol –formaldehyde composite, Novolac resin ,Tg,Tg0

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.