Tribological effect of thermocycling on dental nano-composite
- سال انتشار: 1392
- محل انتشار: کنفرانس دو سالانه بین المللی مکانیک جامدات تجربی
- کد COI اختصاصی: WMECH02_098
- زبان مقاله: انگلیسی
- تعداد مشاهده: 799
نویسندگان
PhD Student
Professor, Fatigue and Fracture Laboratory, Center of Excellence in Experimental Solid Mechanics and Dynamics, School of Mechanical Engineering, Iran University of Science and Technology, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran
چکیده
The effect of thermocycling on the tribological properties of a commercial dental nano-composite has been studied by using the nano-scratch experiment. For this purpose some disk specimens from Filtek Z350 XT (3M ESPE, Germany) nano-composite, each of the diameter 10 mm and the thickness 4 mm were prepared. Half of the specimens were stored in distilled water at ambient conditions and the other half were thermocycled in distilled water for 1000 cycles between temperatures 5°C and 55°C. The nano-scratch experiment was applied on both non-thermocycled and thermocycled specimens by using Triboscope system (Hysitron Inc., USA) and Berkovich indenter. The nano-scratch experiments were performed by both constant and increasing loads for each sample. Atomic force microscopy (AFM) images were taken from the scratch site for analyzing the surface deformation of the samples. The scratch profile, residual scratch depth, scratch hardness and critical scratch load were obtained from the nano-scratch test and AFM images. The results indicate that the residual scratch depth and the criticalscratch load of the thermocycled samples have been decreased compared to the non-thermocycled ones. However, the scratch hardness of the thermocycled samples has been increased in comparison to the non-thermocycled specimens.کلیدواژه ها
Tribological properties; nano-scratch experiment; dental nano-composite; thermocyclingمقالات مرتبط جدید
- Analytical determination of flexural rigidity of thin-walled pultruded composite I-beams
- Matrix-Dominated Damage Process in CFRP Composite Laminates underFlexural Loading Condition
- Indentation Size Scale Effect on Mechanical Properties of Cold SprayCoating
- Determination of Forming Limit Diagrams for Tailor Welded Blanks
- Control of dynamic building façade: design, analysis and experiments
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.