IDENTIFICATION OF DAMAGE MECHANISMS IN GLASS/POLYESTER COMPOSITES UNDER BUCKLING LOADS BY MEANS OF ACOUSTIC EMISSION

  • سال انتشار: 1392
  • محل انتشار: کنفرانس ملی مهندسی مکانیک ایران
  • کد COI اختصاصی: NCMII01_400
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 1115
دانلود فایل این مقاله

نویسندگان

saeid abazary

Department of Mechanical Engineering, Kermanshah Branch, Islamic Azad University, Kermanshah, Iran

morteza dadashzadeh tahunchi

Department of Mechanical Engineering, Islamic Azad University, Gazvin, Iran.

jamal seiedi

Department of Mechanical Engineering, Ilam Branch, Islamic Azad University, Ilam, Iran

Ahmad Doudani

Department of Mechanical Engineering, Kermanshah Branch, Islamic Azad University, Kermanshah, Iran

چکیده

The non-destructive Acoustic Emission (AE) techniques acquire and analyse the signals emitted from the deformation or fracture of materials under external loading. In this study, the AE techniques with statistical analysis were used to study the damage process of composite laminate under buckling loads. Different damage mechanisms are activated within the composite laminate during loading scenario. These ‘‘damage entities’’ are acting in different space and time scales within the service life of the structure and may be interdependent. Loading of composite laminates in particular leads to the accumulation of distinct damage mechanisms, such as matrix cracking, delamination between successive plies and fibre rupture at the final stage of loading. The tested of glass/polyester composite specimens include three lay-up patterns: [0/90]6s, [Woven]6s and [0]6s. Moreover, the microscopic properties of different composite specimens after fracture are watched and analysed by scanning electron microscope (SEM). Based on the SEM conception, the controlling failure mechanisms of composites including the splitting matrix cracking, fibre/matrix interface debonding, fibre pull-out and breakage as well as delamination are identified. Such damage detection of composite parts is very important. Continue to compare our results with The results of the acoustic signal analysis methods in relation to the failure of the buckling load of composite materials such as: The signal processing method, using scanning electron microscope the result of many investigations in the past, has been paid

کلیدواژه ها

Acoustic Emission, Composite Material, Damage Mechanism, SEM

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.