A Comprehensive Study on the Effect of Wire EDM Current Intensity on the Tribological Behavior and Energy Efficiency in Aluminum Machining: A Novel Approach Toward Sustainable Manufacturing
- سال انتشار: 1404
- محل انتشار: مجله شکل دهی مواد، دوره: 12، شماره: 4
- کد COI اختصاصی: JR_IJMF-12-4_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 40
نویسندگان
School of Mechanical Engineering, College of Engineering, University of Tehran, Tehran, Iran
School of Mechanical Engineering, College of Engineering, University of Tehran, Tehran, Iran
Faculty of Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Department of Engineering, Islamic Azad University, Mashhad, Iran
چکیده
This study investigates the influence of discharge current variations in the wire electrical discharge machining (WEDM) process on the surface properties and tribological behavior of aluminum components. Five aluminum samples were machined at current levels ranging from ۱ to ۵ amperes, and their surface roughness, microhardness, wear resistance, and corrosion rate were evaluated. Additionally, the energy consumption per unit volume of material removed was calculated. The results showed that as the current increased from ۱ to ۵ A, surface roughness initially rose from ۱.۸ µm for the reference sample to a maximum of ۳.۵ µm, then decreased to ۲.۵ µm at the highest current. Surface microhardness increased from ۴۹.۸ HV in the reference sample to a maximum of ۵۷ HV. Wear and corrosion rates, key indicators of surface performance, were ۹.۲ mg and ۰.۰۰۸ mm/year under optimal conditions, compared to ۱۸.۴ mg and ۰.۰۰۱ mm/year in the reference sample. Furthermore, specific energy consumption initially decreased but then increased at higher currents due to unstable sparks and re-melting effects. These findings provide valuable insights for optimizing electrical parameters in WEDM parameters to improve the performance and sustainability of machined aluminum components.کلیدواژه ها
Wire EDM, aluminum, Tribological Behavior, energy, Current Intensityاطلاعات بیشتر در مورد COI