High-density polyethylene composites with treated perlite: Thermal and mechanical properties

  • سال انتشار: 1404
  • محل انتشار: فصلنامه پلی اولفین ها، دوره: 12، شماره: 2
  • کد COI اختصاصی: JR_POJ-12-2_003
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 36
دانلود فایل این مقاله

نویسندگان

Linda Gouissem

Département d’Enseignement de Base en Technologie, Faculté de Technologie, Université Ferhat ABBAS Sétif-۱, Sétif ۱۹۰۰۰, Algérie

چکیده

This study explores the development of high-density polyethylene (HDPE) composites reinforced with stearic acid-treated expanded perlite (TEP) to examine their thermal, mechanical, and processing properties. The composites were fabricated using a plastograph at ۲۰۰°C, incorporating perlite concentrations from ۵% to ۲۰% by volume. The effects of stearic acid (SA) treatment and perlite content were analyzed through SEM, melt flow index (MFI), tensile and impact testing, and thermal analysis (DSC, TGA, and Vicat softening temperature). SEM analysis revealed that untreated perlite exhibited a highly porous structure, while HCl treatment induced fragmentation. At ۵% SA, perlite particles were well dispersed with a thin coating, whereas at ۱۰% SA, the coating was more pronounced, leading to agglomeration. The MFI increased with perlite loading, reaching ۱۲.۳ g/۱۰ min at ۲۰% perlite, compared to ۸.۸۸ g/۱۰ min for neat HDPE. Mechanical testing showed that the elastic modulus increased by ۳۶% (۷۸۶ MPa) at ۵% perlite, dropped to ۴۶۰.۸ MPa at ۱۵%, and rose again to ۷۰۷.۷ MPa at ۲۰%, suggesting structural reinforcement. Moderate perlite content (۵-۱۰%) preserved ductility, while higher concentrations (۱۵-۲۰%), especially with ۱۰% SA, increased brittleness due to reduced interfacial adhesion. Thermal analysis showed a slight decrease in melting temperature and a slight increase in crystallization temperature with the addition of treated perlite, while thermal stability improved and the Vicat softening temperature remained unchanged. These results highlight the potential of SA-treated expanded perlite as a viable alternative to conventional fillers, offering a balance between stiffness, ductility, and thermal resistance. The developed composites are promising for light weight and cost-effective applications in energy management and construction.

کلیدواژه ها

Expanded perlite, composites, HDPE, chemical treatment, stearic acid

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.